Thorlabs索雷博 LCC1223T-A 温度稳定型全波液晶延迟器
| Item # | LCC1223T-A | |
|---|---|---|
| Wavelength Range | 350 - 700 nma | |
| Liquid Crystal Material | Nematic Liquid Crystal | |
| Retardance Range | ~30 nm to >λ | |
| Clear Aperture | Ø20 mm | |
| Surface Quality | 40-20 Scratch-Dig | |
| Beam Deviation | < 5 arcmin | |
| Switching Speed (Rise/Fall, Typical)b | 59.6 ms / 1.45 ms @ 22 °C | |
| Damage Threshold | Pulsed (ns) | 1.0 J/cm2 (532 nm, 10 Hz, 8 ns, Ø200 µm) |
| Pulsed (fs) | 0.01 J/cm2 (532 nm, 100 Hz, 76 fs, Ø162 µm) | |
| Wavefront Distortion | ≤λ/4 (@635 nm) | |
| Retardance Uniformity | < λ/50 over the Entire Clear Aperture | |
| Housing Outer Diameter | 2" | |
| Housing Thickness | 12 mm | |
| Storage Temperature | -30 to 70 °C | |
| Operation Temperature | -20 to 45 °C | |
| Compatible Mounts | RSP2 (RSP2/M), LCRM2A (LCRM2/M), KM200 | |
| Temperature Sensor | TH10K 10 kΩ Thermistor | |
| Heater Resistance | 38.4 Ω ±10% | |
| Heating Capacity (Typical) | 15 Watts | |
| Heating Current (Max) | 625 mA (@ 15 W) | |
- 当液晶曝光在接近紫外波长的光源时，更容易受到损伤。我们的测试显示了当液晶可变延迟器曝光在光源为395 nm，6 W/cm2下四小时时，延迟器会发生恶化。当光源为365 nm，40 mW/cm2时，液晶可变延迟器会在15分钟内损坏。因此，推荐液晶可变延迟器在光源为400 nm或更长波长下使用。对于较短的波长，应保持低功率并限制曝光时间。波长越短，液晶越容易受到损伤。
- 响应速度很大程度上取决于多个因素，包括电压变化和液晶单元的温度。更多信息和其它规格请看响应时间标签。
联系电话 : 0755-83317774 移动电话 : 18938648240 Email : 1605935956@qq.com QQ : 1605935956
联系我们 Contact us
联系电话：18938648240
邮箱：1605935956@qq.com
深圳市龙岗区平湖街道禾花社区华南大道一号华南国际印刷纸品包装物流区二期2号楼B1D064
扫一扫加微信
深圳市朗磊贸易有限公司 版权所有